Extensive research of conductivity in the fluorite-like KLn4Mo3O15F (Ln = La, Pr, Nd) rare earth molybdates: theoretical and experimental data.

The conductive properties of fluorite-like structures KLn4Mo3O15F (Ln = La, Pr, Nd: KLM, KPM, KNM) have been studied theoretically and experimentally. Theoretical studies included the geometrical-topological analysis of voids and channels available for migration of working ions; bond valence site energy calculations of the oxygen ions' migration energy; quantum-chemical calculations for the estimation of the oxygen vacancies formation energy. Experimental measurements of conductivity were made using impedance spectroscopy and as a function of oxygen partial pressure. The total conductivity was ∼10-3 S cm-1 for KLM and ∼10-2 S cm-1 for KPM and KNM at 800 °C. Measurements with changes in partial pressure proved the mixed nature of electric transport in KLM, KPM, and KNM phases, with predominantly ionic conductivity. The measured ion transference numbers in air reached approximately 0.9 at 800 °C for the KPM and KNM ceramics. Also, evaluated proton transfer numbers were less than 10%, indicating a small contribution to the total conductivity.

Green nanocomposite gels based on binary network of sodium alginate and percolating halloysite clay nanotubes for 3D printing.

Alginate hydrogels with embedded rigid percolating network of halloysite clay nanotubes were evaluated as a novel ink for 3D printing. Hydrophilic alginate macromolecules adsorbing on halloysite stabilize the network of the nanotubes and form their own network of interlaced polymer chains. The effect of halloysite content on the structure and properties of the hydrogels was studied by rheometry, thermogravimetric analysis, FTIR-spectroscopy, dynamic light scattering, transmission electron microscopy, and 3D cryo-electron microscopy. Hydrogels demonstrate a very pronounced shear-thinning at extrusion and rather quick viscosity recovery after extrusion assigned to rapid rearrangement of the network structure promoted by mobile alginate chains. Even at low volume fractions (up to 0.054) the nanotubes reinforce the hydrogel increasing its storage modulus up to 650 Pa and inducing the appearance of yield stress. These properties make the alginate/halloysite hydrogels promising for the application in 3D printing for fabrication of green and sustainable nanocomposite materials made from natural components.

A New Look at the Chemical Recycling of Polypropylene: Thermal Oxidative Destruction in Aqueous Oxygen-Enriched Medium.

Recycling of plastic waste, in particular polypropylene, represents one of the most pressing challenges facing humanity. Despite the promise of chemical methods for recycling polypropylene, they usually require a high temperature and are energy-intensive. In this work, we investigated the oxidative thermolysis of polypropylene in aqueous media. This approach rendered it possible to carry out the decomposition of the polymer at a comparatively low temperature (150 °C). It was shown that among the tested, the most promising aqueous medium for the decomposition of polypropylene is water saturated with gaseous oxygen at an elevated pressure (14 bar) and at a temperature of 150 °C. In such an environment, polypropylene was converted mostly to acetic acid (up to 1.3 g/g acetic acid to starting polypropylene mass ratio). Moreover, methanol, formic acid, and propionic acid were also detected as the products. Finally, the applicability of the proposed recycling method to real polypropylene waste was shown.

Green approach for fabrication of bacterial cellulose-chitosan composites in the solutions of carbonic acid under high pressure CO2.

The functionalization of the bacterial cellulose (BC) surface with a chitosan biopolymer to expand the areas of possible applications of the modified BC is an important scientific task. The creation of such composites in the carbonic acid solutions that were performed in this work has several advantages in terms of being biocompatible and eco-friendly. Quantitative analysis of chitosan content in the composite was conducted by tritium-labeled chitosan radioactivity detection method and this showed three times increased chitosan loading. Different physicochemical methods showed successful incorporation of chitosan into the BC matrix and interaction with it through hydrogen bonds. Microscopy results showed that the chitosan coating with a thickness of around 10 nm was formed in the bulk of BC, covering each microfibril. It was found that the inner specific surface area increased 1.5 times on deposition of chitosan from the solutions in carbonic acid.

Synthesis, structure and properties of layered Pr2MoO6-based oxymolybdates doped with Mg.

Undoped and Mg-doped Pr2MoO6 oxymolybdate polycrystals and single crystals have been prepared by solid-state reactions and flux growth. The compounds have been characterized by powder X-ray diffraction, energy-dispersive spectroscopy, inductively coupled plasma mass spectrometry, scanning transmission electron microscopy, single crystal X-ray structure analysis, differential scanning calorimetry and thermogravimetry. The (MgO)x(Pr2O3)y(MoO3)z (x + y + z = 1) solid solution series has been shown to extend to x = 0.03. The structure of the Mg-doped Pr2MoO6 single crystals can be represented as superimposed lattices of the main matrix (Pr2MoO6) and lattices in which Mo atoms are partially replaced by Mg. The incorporation of Mg atoms into the structure of Pr2MoO6 results in the disordering of the praseodymium and oxygen lattices. Both the polycrystalline and single-crystal Mg-doped samples are hygroscopic.

Structural organization of bacterial cellulose: The origin of anisotropy and layered structures.

In this paper, we perform a systematic analysis of the structural organization of bacterial cellulose (BC). We report four types of organization of the BC mass, produced by Gluconacetobacter hansenii that occur depending on cultivation conditions. Two of those, particularly, plywood type one and layers of micro-sized tubes were observed and described for the first time. In spherical BC particles (pellets), we found the layered structure that had previously been reported for planar geometry only. We suggest a model explaining why layers form in BC films and attempt to reveal the impact of different factors on the BC microscale morphology. We assume that the main factor that has direct impact on the type of structure formed is the rate of BC mass accumulation.

Structure of fluorite-like compound based on Nd5Mo3O16 with lead partly substituting for neodymium.

A single crystal of Nd5Mo3O16 with lead partly substituting for neodymium, which has a fluorite-like structure, was studied by precision X-ray diffraction, high-resolution transmission microscopy and EDX microanalysis. The crystal structure is determined in the space group Pn3¯n. It was found that the Pb atoms substitute in part for Nd atoms in the structure and are located in the vicinity of Nd2 positions. Partial substitutions of Mo cations for Nd positions and of Nd for Mo positions in crystals of the Ln5Mo3O16 oxide family are corroborated by X-ray diffraction for the first time. The first experimental verification of the location of an additional oxygen ion in the voids abutting MoO4 tetrahedra was obtained.

X-ray diffraction study of oxygen-conducting compounds Ln2Mo2O9 (Ln = La, Pr).

The La2Mo2O9 (LM) and Pr2Mo2O9 (PM) single crystals are studied using precision X-ray diffraction and high-resolution transmission microscopy at room temperature. The crystal structures are determined in the space group P2(1)3. La and Pr atoms, as well as Mo1 and O1 atoms, are located in the vicinity of the threefold axes rather than on the axes as in the high-temperature cubic phase. In both structures studied, the O2 and O3 positions are partially occupied. The coexistence of different configurations of the Mo coordination environment facilitates the oxygen-ion migration in the structure. Based on the X-ray data, the activation energies of O atoms are calculated and the migration paths of oxygen ions in the structures are analysed. The conductivity of PM crystals is close to that of LM crystals. The O2 and O3 atoms are the main contributors to the ion conductivity of LM and PM.

Novel composite Zr/PBI-O-PhT membranes for HT-PEFC applications.

Novel composite membranes for high temperature polymer-electrolyte fuel cells (HT-PEFC) based on a poly[oxy-3,3-bis(4'-benzimidazol-2″-ylphenyl)phtalide-5″(6″)-diyl] (PBI-O-PhT) polymer with small amounts of added Zr were prepared. It was shown in a model reaction between zirconium acetylacetonate (Zr(acac)4) and benzimidazole (BI) that Zr-atoms are capable to form chemical bonds with BI. Thus, Zr may be used as a crosslinking agent for PBI membranes. The obtained Zr/PBI-O-PhT composite membranes were examined by means of SAXS, thermomechanical analysis (TMA), and were tested in operating fuel cells by means of stationary voltammetry and impedance spectroscopy. The new membranes showed excellent stability in a 2000-hour fuel cell (FC) durability test. The modification of the PBI-O-PhT films with Zr facilitated an increase of the phosphoric acid (PA) uptake by the membranes, which resulted in an up to 2.5 times increased proton conductivity. The existence of an optimal amount of Zr content in the modified PBI-O-PhT film was shown. Larger amounts of Zr lead to a lower PA doping level and a reduced conductivity due to an excessively high degree of crosslinking.

Cell attachment on poly(3-hydroxybutyrate)-poly(ethylene glycol) copolymer produced by Azotobacter chroococcum 7B.

BACKGROUND: The improvement of biomedical properties, e.g. biocompatibility, of poly(3-hydroxyalkanoates) (PHAs) by copolymerization is a promising trend in bioengineering. We used strain Azotobacter chroococcum 7B, an effective producer of PHAs, for biosynthesis of not only poly(3-hydroxybutyrate) (PHB) and its main copolymer, poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHB-HV), but also alternative copolymer, poly(3-hydroxybutyrate)-poly(ethylene glycol) (PHB-PEG). RESULTS: In biosynthesis we used sucrose as the primary carbon source and valeric acid or poly(ethylene glycol) 300 (PEG 300) as additional carbon sources. The chemical structure of PHB-PEG and PHB-HV was confirmed by 1H nuclear-magnetic resonance (1H NMR) analysis. The physico-chemical properties (molecular weight, crystallinity, hydrophilicity, surface energy) and surface morphology of films from PHB copolymers were studied. To study copolymers biocompatibility in vitro the protein adsorption and COS-1 fibroblasts growth on biopolymer films by XTT assay were analyzed. Both copolymers had changed physico-chemical properties compared to PHB homopolymer: PHB-HV and PHB-PEG had less crystallinity than PHB; PHB-HV was more hydrophobic than PHB in contrast to PHB-PEG appeared to have greater hydrophilicity than PHB; whereas the morphology of polymer films did not differ significantly. The protein adsorption to PHB-PEG was greater and more uniform than to PHB and PHB-PEG copolymer promoted better growth of COS-1 fibroblasts compared with PHB homopolymer. CONCLUSIONS: Thus, despite low EG-monomers content in bacterial origin PHB-PEG copolymer, this polymer demonstrated significant improvement in biocompatibility in contrast to PHB and PHB-HV copolymers, which may be coupled with increased protein adsorption and hydrophilicity of PEG-containing copolymer.